B.A.Loginov, Y.V.Khripunov, M.A.Shcherbina, A.O.Vyunik, V.D.Dmitrieva, A.A.Dyakova, M.K.Lebedeva, V.S.Makeev, A.R.Pervykh, D.S.Shevchenko, S.D.Khanin
OBSERVATION OF CHANGES IN MORPHOLOGY OF HIGH-TEMPERATURE METAL FILMS IN A SCANNING PROBE MICROSCOPE DURING WARMING UP IN OPEN SPACE CONDITIONS Regularities of changes in the surface morphology of high-temperature metal coatings used as protective coatings can be applied to the structures of spacecraft sent closer to the Sun, have been observed. It is shown that films become less friable, and small grains of these films increase in size, as if spreading on the surface and rearranging into larger formations.
OBSERVATION OF CHANGES IN MORPHOLOGY OF HIGH-TEMPERATURE METAL FILMS IN A SCANNING PROBE MICROSCOPE DURING WARMING UP IN OPEN SPACE CONDITIONS Regularities of changes in the surface morphology of high-temperature metal coatings used as protective coatings can be applied to the structures of spacecraft sent closer to the Sun, have been observed. It is shown that films become less friable, and small grains of these films increase in size, as if spreading on the surface and rearranging into larger formations.
Б.А.Логинов, Ю.В.Хрипунов, М.А.Щербина, А.О.Вьюник, В.Д.Дмитриева, А.А.Дьякова, М.К.Лебедева, В.С.Макеев, А.Р.Первых, Д.С.Шевченко, С.Д.Ханин
НАБЛЮДЕНИЕ ИЗМЕНЕНИЯ МОРФОЛОГИИ ПЛЕНОК ВЫСОКОТЕМПЕРАТУРНЫХ МЕТАЛЛОВ В СКАНИРУЮЩЕМ ЗОНДОВОМ МИКРОСКОПЕ ПРИ ПРОГРЕВЕ В УСЛОВИЯХ ОТКРЫТОГО КОСМОСА Наблюдены закономерности изменения морфологии поверхности покрытий из высокотемпературных металлов, которые в качестве защитных покрытий могут наноситься на конструкции космических аппаратов, посылаемых ближе к Солнцу. Показано, что пленки при этом становятся менее рыхлыми, а мелкие зерна этих пленок увеличиваются по размеру, как бы растекаясь по поверхности и перестраиваясь в более крупные образования.
НАБЛЮДЕНИЕ ИЗМЕНЕНИЯ МОРФОЛОГИИ ПЛЕНОК ВЫСОКОТЕМПЕРАТУРНЫХ МЕТАЛЛОВ В СКАНИРУЮЩЕМ ЗОНДОВОМ МИКРОСКОПЕ ПРИ ПРОГРЕВЕ В УСЛОВИЯХ ОТКРЫТОГО КОСМОСА Наблюдены закономерности изменения морфологии поверхности покрытий из высокотемпературных металлов, которые в качестве защитных покрытий могут наноситься на конструкции космических аппаратов, посылаемых ближе к Солнцу. Показано, что пленки при этом становятся менее рыхлыми, а мелкие зерна этих пленок увеличиваются по размеру, как бы растекаясь по поверхности и перестраиваясь в более крупные образования.
A.I.Akhmetova, T.O.Sovetnikov, B.A.Loginov, D.I.Yaminsky, I.V.Yaminsky
QUARTZ REFERENCE MEASURE FOR SCANNING PROBE MICROSCOPY Improving accuracy and reliability of measurements at the nanoscale is becoming increasingly important for various applications, especially in areas such as semiconductor electronics, optical metamaterials, sensors, and biological measurements. With the development of high-resolution imaging techniques, the need for metrological verification of these devices has also naturally arisen. The challenge of measuring nanoscale morphology at a specific location has emerged, which requires positional accuracy in both vertical and lateral directions. Stability and robustness of measurements require that the microscope should be regularly calibrated using calibration tools. Quartz calibration measures can be one such standard.
QUARTZ REFERENCE MEASURE FOR SCANNING PROBE MICROSCOPY Improving accuracy and reliability of measurements at the nanoscale is becoming increasingly important for various applications, especially in areas such as semiconductor electronics, optical metamaterials, sensors, and biological measurements. With the development of high-resolution imaging techniques, the need for metrological verification of these devices has also naturally arisen. The challenge of measuring nanoscale morphology at a specific location has emerged, which requires positional accuracy in both vertical and lateral directions. Stability and robustness of measurements require that the microscope should be regularly calibrated using calibration tools. Quartz calibration measures can be one such standard.
А.И.Ахметова, Т.О.Советников, Б.А.Логинов, Д.И.Яминский, И.В.Яминский
КВАРЦЕВАЯ ЭТАЛОННАЯ МЕРА ДЛЯ СКАНИРУЮЩЕЙ ЗОНДОВОЙ МИКРОСКОПИИ Повышение точности и достоверности измерений в наномасштабе становится все более актуальной задачей для различных приложений, особенно в таких областях, как полупроводниковая электроника, оптические метаматериалы, сенсоры и биологические измерения. С появлением методов визуализации высокого разрешения закономерно возникла и потребность в метрологической поверке этих приборов. Появилась задача измерить наноразмерную морфологию в конкретном местоположении, что требует точности позиционирования как в вертикальном, так и в латеральном направлении. Стабильность и надежность измерений требуют регулярно отлаживать микроскоп с помощью калибровочных средств. Одним из таких эталонов могут быть кварцевые калибровочные меры.
КВАРЦЕВАЯ ЭТАЛОННАЯ МЕРА ДЛЯ СКАНИРУЮЩЕЙ ЗОНДОВОЙ МИКРОСКОПИИ Повышение точности и достоверности измерений в наномасштабе становится все более актуальной задачей для различных приложений, особенно в таких областях, как полупроводниковая электроника, оптические метаматериалы, сенсоры и биологические измерения. С появлением методов визуализации высокого разрешения закономерно возникла и потребность в метрологической поверке этих приборов. Появилась задача измерить наноразмерную морфологию в конкретном местоположении, что требует точности позиционирования как в вертикальном, так и в латеральном направлении. Стабильность и надежность измерений требуют регулярно отлаживать микроскоп с помощью калибровочных средств. Одним из таких эталонов могут быть кварцевые калибровочные меры.
Теги: атомно-силовая микроскопия зондовая микроскопия кварцевая эталонная мера метрология сканирующая капиллярная микроскопия эталон нанометра
A.A.Terentyev, A.V.Smirnov
STUDY OF POSSIBILITY OF FLEXIBLE VARIABLE VESSELS FOR REMOTE PRESSURE MEASUREMENT SYSTEMS The technology of silicon deposition has been developed, and it has been possible to obtain a durable polycrystalline silicon film with good adhesion on a PET substrate with a thickness of 150...200 nm. Using this technology, a prototype of a flexible variable capacitance was prepared. The study of capacitance changes due to changes in pressure acting on it has a linear form, which makes it possible to use this technology for the manufacture of a pressure sensor.
STUDY OF POSSIBILITY OF FLEXIBLE VARIABLE VESSELS FOR REMOTE PRESSURE MEASUREMENT SYSTEMS The technology of silicon deposition has been developed, and it has been possible to obtain a durable polycrystalline silicon film with good adhesion on a PET substrate with a thickness of 150...200 nm. Using this technology, a prototype of a flexible variable capacitance was prepared. The study of capacitance changes due to changes in pressure acting on it has a linear form, which makes it possible to use this technology for the manufacture of a pressure sensor.
А.А.Терентьев, А.В.Смирнов
ИССЛЕДОВАНИЯ ВОЗМОЖНОСТИ СОЗДАНИЯ ПЕРЕМЕННЫХ ЕМКОСТЕЙ НА ГИБКОЙ ОСНОВЕ ДЛЯ СИСТЕМ ДИСТАНЦИОННОГО ИЗМЕРЕНИЯ ДАВЛЕНИЯ Аннотация. Отработана технология напыления кремния, удалось получить прочную поликристаллическую пленку кремния, обладающую хорошей адгезией на подложке ПЭТ толщиной 150…200 нм. С помощью данной технологии был изготовлен опытный образец гибкой переменной емкости. Исследование изменения емкости от изменения воздействующего на него давления имеет линейный вид, что позволяет открывает возможность использования данной технологии для изготовления датчика давления.
ИССЛЕДОВАНИЯ ВОЗМОЖНОСТИ СОЗДАНИЯ ПЕРЕМЕННЫХ ЕМКОСТЕЙ НА ГИБКОЙ ОСНОВЕ ДЛЯ СИСТЕМ ДИСТАНЦИОННОГО ИЗМЕРЕНИЯ ДАВЛЕНИЯ Аннотация. Отработана технология напыления кремния, удалось получить прочную поликристаллическую пленку кремния, обладающую хорошей адгезией на подложке ПЭТ толщиной 150…200 нм. С помощью данной технологии был изготовлен опытный образец гибкой переменной емкости. Исследование изменения емкости от изменения воздействующего на него давления имеет линейный вид, что позволяет открывает возможность использования данной технологии для изготовления датчика давления.
Е.V.Dubrovin,О.N.Koroleva, N.V.Kuzmina, V.L.Drutsa
STUDY OF INFLUENZA A VIRUS NUCLEAR EXPORT PROTEIN AGGREGATES USING ATOMIC FORCE MICROSCOPY The nuclear export protein (NEP) plays an important role in intracellular processes during infection of host cells. In this paper, aggregates of various morphologies and sizes were identified and characterized for the first time using atomic force microscopy. The results obtained may be used for development of new antiviral drugs and developing of NEP-based drug delivery systems.
STUDY OF INFLUENZA A VIRUS NUCLEAR EXPORT PROTEIN AGGREGATES USING ATOMIC FORCE MICROSCOPY The nuclear export protein (NEP) plays an important role in intracellular processes during infection of host cells. In this paper, aggregates of various morphologies and sizes were identified and characterized for the first time using atomic force microscopy. The results obtained may be used for development of new antiviral drugs and developing of NEP-based drug delivery systems.
Е.В.Дубровин, О.Н.Королева, Н.В.Кузьмина, В.Л.Друца
ИССЛЕДОВАНИЕ АГРЕГАТОВ БЕЛКА ЯДЕРНОГО ЭКСПОРТА ВИРУСА ГРИППА А С ПОМОЩЬЮ АТОМНО-СИЛОВОЙ МИКРОСКОПИИ Белок ядерного экспорта (NEP) играет важную роль во внутриклеточных процессах при инфицировании клеток хозяина. В данной работе впервые с помощью атомно-силовой микроскопии выявлены и охарактеризованы агрегаты различной морфологии и размеров. Полученные результаты могут быть востребованы для разработки новых противовирусных препаратов и создания систем доставки лекарственных средств на основе NEP.
ИССЛЕДОВАНИЕ АГРЕГАТОВ БЕЛКА ЯДЕРНОГО ЭКСПОРТА ВИРУСА ГРИППА А С ПОМОЩЬЮ АТОМНО-СИЛОВОЙ МИКРОСКОПИИ Белок ядерного экспорта (NEP) играет важную роль во внутриклеточных процессах при инфицировании клеток хозяина. В данной работе впервые с помощью атомно-силовой микроскопии выявлены и охарактеризованы агрегаты различной морфологии и размеров. Полученные результаты могут быть востребованы для разработки новых противовирусных препаратов и создания систем доставки лекарственных средств на основе NEP.
Теги: atomic force microscopy influenza a virus nuclear export protein protein aggregation агрегация белка атомно-силовая микроскопия белок ядерного экспорта вирус гриппа а
Nanomaterials
Наноматериалы
A.B.Golik, A.A.Nagdalian, A.V.Blinov, R.Sh.Zakaeva, P.S.Leontev, M.A.Taravanov, Z.A.Rekhman, A.S.Askerova
STUDY OF THE PROCESS OF FORMATION OF COPPER OXIDE NANOPARTICLES STABILIZED BY GLYCERYL COCOATE In this work, samples of nanoscale copper oxide stabilised with glyceryl cocoate were prepared by chemical precipitation in aqueous medium. Scanning electron microscopy microstructure studies showed that the copper oxide sample is represented by irregularly shaped agglomerates of size from 1 to 30 μm, which consist of nanoparticles diameters from 5 to 50 nm. Phase composition studies showed that the obtained sample is copper (II) oxide with monoclinic-beta crystal lattice, in this case the space group corresponds to C2/c. As a result of computer quantum-chemical modelling of interaction between glyceryl cocoate and copper oxide, it was found that the presented compound is energetically favourable (∆E = 1714.492 kcal/mol) and the interaction occurs via the carboxylate anion. This compound possesses a chemical rigidity value η ≥ 0.050 eV, indicating its stability. Interaction between glyceryl cocoate and copper oxide was found to occur through the carboxyl group by IR spectroscopy. During optimisation of the synthesis technique, it was found that the optimal parameters for obtaining CuO nanoparticles with an average hydrodynamic radius of less than 200 nm are temperatures in the rage of 95 to 100 °C, mass of copper acetate from 3 to 4 grams and concentration of stabiliser PEG-7 from 1–3%.
STUDY OF THE PROCESS OF FORMATION OF COPPER OXIDE NANOPARTICLES STABILIZED BY GLYCERYL COCOATE In this work, samples of nanoscale copper oxide stabilised with glyceryl cocoate were prepared by chemical precipitation in aqueous medium. Scanning electron microscopy microstructure studies showed that the copper oxide sample is represented by irregularly shaped agglomerates of size from 1 to 30 μm, which consist of nanoparticles diameters from 5 to 50 nm. Phase composition studies showed that the obtained sample is copper (II) oxide with monoclinic-beta crystal lattice, in this case the space group corresponds to C2/c. As a result of computer quantum-chemical modelling of interaction between glyceryl cocoate and copper oxide, it was found that the presented compound is energetically favourable (∆E = 1714.492 kcal/mol) and the interaction occurs via the carboxylate anion. This compound possesses a chemical rigidity value η ≥ 0.050 eV, indicating its stability. Interaction between glyceryl cocoate and copper oxide was found to occur through the carboxyl group by IR spectroscopy. During optimisation of the synthesis technique, it was found that the optimal parameters for obtaining CuO nanoparticles with an average hydrodynamic radius of less than 200 nm are temperatures in the rage of 95 to 100 °C, mass of copper acetate from 3 to 4 grams and concentration of stabiliser PEG-7 from 1–3%.
А.Б.Голик, А.А.Нагдалян, А.В.Блинов, Р.Ш.Закаева, П.С.Леонтьев, М.А.Тараванов, З.А.Рехман, А.С.Аскерова
ИССЛЕДОВАНИЕ ПРОЦЕССА ФОРМИРОВАНИЯ НАНОЧАСТИЦ ОКСИДА МЕДИ, СТАБИЛИЗИРОВАННЫХ ГЛИЦЕРИЛ КОКОАТОМ В данной работе образцы наноразмерного оксида меди, стабилизированного глицерил кокоатом, получали методом химического осаждения в водной среде. Исследования микроструктуры методом сканирующей электронной микроскопии показали, что образец оксида меди представлен агломератами неправильной формы размером от 1 до 30 мкм, которые состоят из наночастиц диаметром от 5 до 50 нм. Исследования фазового состава показали, что полученный образец представляет собой оксид меди (II) с кристаллической моноклинной-бета-решеткой, в данном случае пространственная группа соответствует C2/с. В результате компьютерного квантово-химического моделирования взаимодействия глицерил кокоата и оксида меди установили, что представленное соединение является энергетически выгодным (∆E = 1714,492 ккал/моль) и взаимодействие происходит через карбоксилат-анион. Данное соединение обладает значением химической жесткости η ≥ 0,050 эВ, что свидетельствует о его стабильности. Методом ИК-спектроскопии было установлено, что взаимодействие глицерил кокоата и оксида меди происходит через карбоксильную группу. В ходе оптимизации методики синтеза было установлено, что для получения НЧ CuO со средним гидродинамическим радиусом менее 200 нм оптимальными параметрами являются температура от 95 до 100 °С, масса ацетата меди от 3 до 4 г и концентрация стабилизатора ПЭГ-7 от 1–3%.
ИССЛЕДОВАНИЕ ПРОЦЕССА ФОРМИРОВАНИЯ НАНОЧАСТИЦ ОКСИДА МЕДИ, СТАБИЛИЗИРОВАННЫХ ГЛИЦЕРИЛ КОКОАТОМ В данной работе образцы наноразмерного оксида меди, стабилизированного глицерил кокоатом, получали методом химического осаждения в водной среде. Исследования микроструктуры методом сканирующей электронной микроскопии показали, что образец оксида меди представлен агломератами неправильной формы размером от 1 до 30 мкм, которые состоят из наночастиц диаметром от 5 до 50 нм. Исследования фазового состава показали, что полученный образец представляет собой оксид меди (II) с кристаллической моноклинной-бета-решеткой, в данном случае пространственная группа соответствует C2/с. В результате компьютерного квантово-химического моделирования взаимодействия глицерил кокоата и оксида меди установили, что представленное соединение является энергетически выгодным (∆E = 1714,492 ккал/моль) и взаимодействие происходит через карбоксилат-анион. Данное соединение обладает значением химической жесткости η ≥ 0,050 эВ, что свидетельствует о его стабильности. Методом ИК-спектроскопии было установлено, что взаимодействие глицерил кокоата и оксида меди происходит через карбоксильную группу. В ходе оптимизации методики синтеза было установлено, что для получения НЧ CuO со средним гидродинамическим радиусом менее 200 нм оптимальными параметрами являются температура от 95 до 100 °С, масса ацетата меди от 3 до 4 г и концентрация стабилизатора ПЭГ-7 от 1–3%.
Теги: chemical deposition copper oxide ir-spectroscopy nanoparticles stabiliser ик-спектроскопия наночастицы оксид меди стабилизатор химическое осаждение
Equipment for nanoindustry
Оборудование для наноиндустрии
A.F.Akhkiamova, A.F.Abukaev, I.I.Rulev, A.Y.Konyakhina, A.P.Melnikov, D.A.Ivanov
COMBINING NANOCALORIMETRY AND ATOMIC FORCE MICROSCOPY TO STUDY STRUCTURE FORMATION PROCESSES ON THE NANOSCALE Wide range of rapid analytical methods intended for the physicochemical analysis of organic compounds are being actively developed. The present paper highlights the possibility of studying microquantities of polymer materials using a chip calorimetry (nanocalorimetry) method combined with atomic force microscopy (AFM). An experimental setup is presented for conducting combined studies using ultrafast chip calorimetry and AFM. The main technological aspects of combining the two methods are considered, and behavior of a nanocalorimetric sensor when interacting with a cold AFM cantilever for measurements of microquantities of polymer materials at different temperatures is addressed in situ.
COMBINING NANOCALORIMETRY AND ATOMIC FORCE MICROSCOPY TO STUDY STRUCTURE FORMATION PROCESSES ON THE NANOSCALE Wide range of rapid analytical methods intended for the physicochemical analysis of organic compounds are being actively developed. The present paper highlights the possibility of studying microquantities of polymer materials using a chip calorimetry (nanocalorimetry) method combined with atomic force microscopy (AFM). An experimental setup is presented for conducting combined studies using ultrafast chip calorimetry and AFM. The main technological aspects of combining the two methods are considered, and behavior of a nanocalorimetric sensor when interacting with a cold AFM cantilever for measurements of microquantities of polymer materials at different temperatures is addressed in situ.
А.Ф.Ахкямова, А.Ф.Абукаев, И.И.Рулев, А.Ю.Коняхина, А.П.Мельников, Д.А.Иванов
СОВМЕЩЕНИЕ МЕТОДОВ НАНОКАЛОРИМЕТРИИ И АТОМНО-СИЛОВОЙ МИКРОСКОПИИ ДЛЯ ИССЛЕДОВАНИЯ СТРУКТУРООБРАЗОВАНИЯ НА НАНОШКАЛЕ На данный момент активно развивается широкий спектр аналитических экспресс-методов, предназначенных для физико-химического анализа органических соединений. В данной работе показана возможность исследования микроколичеств полимерных материалов с использованием метода нанокалориметрии на чипе, совмещенного с атомно-силовой микроскопией. В работе создана экспериментальная установка для проведения совмещенных исследований методами сверхбыстрой калориметрии на чипе (нанокалориметрии) и атомно-силовой микроскопии (АСМ), рассмотрены основные технологические аспекты совмещения двух методов, и изучено поведение нанокалориметрического сенсора при взаимодействии с холодным кантилевером АСМ в ходе измерений in situ микроколичеств полимерных материалов при различных температурах.
СОВМЕЩЕНИЕ МЕТОДОВ НАНОКАЛОРИМЕТРИИ И АТОМНО-СИЛОВОЙ МИКРОСКОПИИ ДЛЯ ИССЛЕДОВАНИЯ СТРУКТУРООБРАЗОВАНИЯ НА НАНОШКАЛЕ На данный момент активно развивается широкий спектр аналитических экспресс-методов, предназначенных для физико-химического анализа органических соединений. В данной работе показана возможность исследования микроколичеств полимерных материалов с использованием метода нанокалориметрии на чипе, совмещенного с атомно-силовой микроскопией. В работе создана экспериментальная установка для проведения совмещенных исследований методами сверхбыстрой калориметрии на чипе (нанокалориметрии) и атомно-силовой микроскопии (АСМ), рассмотрены основные технологические аспекты совмещения двух методов, и изучено поведение нанокалориметрического сенсора при взаимодействии с холодным кантилевером АСМ в ходе измерений in situ микроколичеств полимерных материалов при различных температурах.
Теги: atomic force microscopy microelectromechanical systems nanocalorimetry ultrafast calorimetry атомно-силовая микроскопия микроэлектромеханические системы нанокалориметрия сверхбыстрая калориметрия
A.I.Akhmetova, A.D.Terentev, S.A.Senotrusova, T.O.Sovetnikov, D.I.Yaminsky, V.V.Popov, I.V.Yaminsky
DIFFRACTION GRATING AS A MEANS OF METROLOGICAL SUPPORT OF MICROSCOPY DOI: 10.22184/1993-8578.2024.17.2.128.133
Abstract. Visualization of biomedical samples in their natural environment at micro- and nanoscale is crucial for studying fundamental principles of biosystems functioning with complex interactions. The study of dynamic biological processes requires a microscopic system with multiple measurement capabilities, high spatial and temporal resolution, versatile visualization environments and local manipulation options. Scanning capillary microscopy and microlens microscopy are promising tools for these tasks, but correct operation of either technique is impossible without metrological support. This paper demonstrates the possibility of using a diffraction grating sample for these purposes.
DIFFRACTION GRATING AS A MEANS OF METROLOGICAL SUPPORT OF MICROSCOPY DOI: 10.22184/1993-8578.2024.17.2.128.133
Abstract. Visualization of biomedical samples in their natural environment at micro- and nanoscale is crucial for studying fundamental principles of biosystems functioning with complex interactions. The study of dynamic biological processes requires a microscopic system with multiple measurement capabilities, high spatial and temporal resolution, versatile visualization environments and local manipulation options. Scanning capillary microscopy and microlens microscopy are promising tools for these tasks, but correct operation of either technique is impossible without metrological support. This paper demonstrates the possibility of using a diffraction grating sample for these purposes.
А.И.Ахметова, А.Д.Терентьев, С.А.Сенотрусова, Т.О.Советников, Д.И.Яминский, В.В.Попов, И.В.Яминский
ДИФРАКЦИОННАЯ РЕШЕТКА КАК СРЕДСТВО МЕТРОЛОГИЧЕСКОГО СОПРОВОЖДЕНИЯ МИКРОСКОПИИ DOI: 10.22184/1993-8578.2024.17.2.128.133
Визуализация биомедицинских образцов в их естественной среде в микро- и наномасштабе имеет решающее значение для изучения фундаментальных принципов функционирования биосистем со сложным взаимодействием. Для изучения динамических биологических процессов требуется микроскопическая система с множеством измерительных возможностей, высоким пространственным и временным разрешением, универсальными средами визуализации и возможностями локального манипулирования. Перспективными инструментами для этих задач являются сканирующая капиллярная микроскопия и микролинзовая микроскопия, однако корректная работа ни одной из этих методик невозможна без метрологического сопровождения. В данной работе демонстрируется возможность использования для этих целей образца дифракционной решетки.
ДИФРАКЦИОННАЯ РЕШЕТКА КАК СРЕДСТВО МЕТРОЛОГИЧЕСКОГО СОПРОВОЖДЕНИЯ МИКРОСКОПИИ DOI: 10.22184/1993-8578.2024.17.2.128.133
Визуализация биомедицинских образцов в их естественной среде в микро- и наномасштабе имеет решающее значение для изучения фундаментальных принципов функционирования биосистем со сложным взаимодействием. Для изучения динамических биологических процессов требуется микроскопическая система с множеством измерительных возможностей, высоким пространственным и временным разрешением, универсальными средами визуализации и возможностями локального манипулирования. Перспективными инструментами для этих задач являются сканирующая капиллярная микроскопия и микролинзовая микроскопия, однако корректная работа ни одной из этих методик невозможна без метрологического сопровождения. В данной работе демонстрируется возможность использования для этих целей образца дифракционной решетки.
Теги: дифракционная решетка живые системы метрология микролинзовая микроскопия сканирующая капиллярная микроскопия
Economics
Экономика
A.Yu.Pronin
INDUSTRY 5.0 – A NEW VECTOR OF INDUSTRIAL DEVELOPMENT doi 10.22184/1993-8578.2024.17.2.134.142
The main reasons for transition to a new stage of industrial and economic development are considered, and a comparative analysis of the main conceptual provisions of Industry 4.0 and Industry 5.0 is provided. The basic principles of industrial development in the conditions of transition to Industry 5.0 are formulated.
INDUSTRY 5.0 – A NEW VECTOR OF INDUSTRIAL DEVELOPMENT doi 10.22184/1993-8578.2024.17.2.134.142
The main reasons for transition to a new stage of industrial and economic development are considered, and a comparative analysis of the main conceptual provisions of Industry 4.0 and Industry 5.0 is provided. The basic principles of industrial development in the conditions of transition to Industry 5.0 are formulated.
А.Ю.Пронин
"ИНДУСТРИЯ 5.0" – НОВЫЙ ВЕКТОР ПРОМЫШЛЕННОГО РАЗВИТИЯ doi 10.22184/1993-8578.2024.17.2.134.142
Рассматриваются основные причины перехода к новому этапу развития промышленности и экономики, приведен сравнительный анализ основных концептуальных положений "Индустрии 4.0" и "Индустрии 5.0". Сформулированы основные принципы развития промышленности в условиях перехода к "Индустрии 5.0".
"ИНДУСТРИЯ 5.0" – НОВЫЙ ВЕКТОР ПРОМЫШЛЕННОГО РАЗВИТИЯ doi 10.22184/1993-8578.2024.17.2.134.142
Рассматриваются основные причины перехода к новому этапу развития промышленности и экономики, приведен сравнительный анализ основных концептуальных положений "Индустрии 4.0" и "Индустрии 5.0". Сформулированы основные принципы развития промышленности в условиях перехода к "Индустрии 5.0".